Coated brazing alloy to join all type of steel, stainless steel, Cu alloy, cast iron and specially galvanized steel
Applications:
Typical Mechanical Properties:
Bonding Temperature: 8500C
Tensile Strength: 48 Kg/mm2(68,000 psi)
Flux coated brazing alloy suitable for joining of dissimilar steel to Cu alloy including Ni enhanced high strength bronzes
Applications:
Typical Mechanical Properties:
Bonding Temperature: 875 Deg C
Tensile Shear Strength: 50 Kg/mm2
(1,05,000 psi)
Low temperature silver brazing alloy for high strength joining of dissimilar metals
Applications:
Typical Mechanical Properties:
Rod: 1.6, 2.0, 3.15mm
Shim: 25mm x 0.075 mm
Bonding Temperature: 660 Deg C
Tensile Strength: 45 Kg/mm2(63,000 psi)
Torch brazing rod for self-fluxing copper-to-copper joints
Applications:
Typical Mechanical Properties:
Bonding Temperature : 650 Deg C
Tensile Strength : 37 Kg/mm2 (52,000 psi)
High silver brazing alloy with excellent fluidity for brazing narrow clearance joints
Applications:
Typical Mechanical Properties:
Bonding Temperature : 600 Deg C
Tensile Strength: 65 Kg/mm2 (92,000 psi)
An advanced brazing rod for high strength joining of aluminium parts
Applications:
Typical Mechanical Properties:
Bonding Temperature: 570 Deg C
Tensile Strength: 25 Kg/mm2 (35,000 psi)
Flux coated brazing alloy for built up & overlay application on all ferrous and non-ferrous alloys
Applications:
Typical Mechanical Properties:
Hardness: 95 HRb
Bonding Temperature: 875 Deg C
Tensile Strength: 62 Kg/mm2 (87,000 psi)
Composite gas brazing filler rod with hard carbides embedded in tough matrix
Applications:
Typical Mechanical Properties:
Hardness: Matrix – 210 BHN,
Carbides – 1250 HV (min)